Property

Testing Standard

Condition

Requirement

Tensile Strength

ASTM D412 Die C; AS 1180.2; BS 903.A2;

ISO 37; JIS K6301 Item 3, Dumbell 3

Original 

16MPa (Min)

Aged from 96Hours at 70°C

12.8MPa  (Min)

DIN 53504

Original

15N/mm2 (Min)

Aged for 168 hours at 70°C

12.75N/mm2 (Min)

Elongation at Break

ASTM D412 Die C; AS 1180.2; BS 903.A2;

ISO 37; JIS K6301 Item 3, Dumbell 3

Original 

400% (Min)

Aged for 96 hours at 70°C

320% (Min)

DIN 53504

Original

300% (Min)

Aged for 168 hours at 70°C

280% (Min)

Hardness

ASTM D2240; AS 1683.15.2; BS 903.A6; 

ISO 815; JIS K6301 Item 5A Tester

Original

78° (Max) Shore A

Aged for 96 Hours at 70°C

Original Value + 6°

points increase

DIN 53505

Original

75° (Max) Shore A

Aged for 168 hours at 70°C

Original Value + 5°

points increase

Compression Set

ASTM D395; AS 1683.13B; BS 903.A6; 

ISO 815; JIS K6301 Item 10

Aged for 22 hours at 70°C

30% (Max)

DIN 53517

Aged for 24 hours at 70°C 

40% (Max)

Tear Resistance

ASTM D624; AS 1683.12; BS 903.A3; 

ISO 34.1; JIS K6301 Item 9, Test Piece A

Die B

70kN/m (Min)

DIN 53507

80 N/cm (Min)

Ozone Resistance

ASTM D1149; AS 1683.24; 

BS 903.A43; DIN 53509; ISO 143/1

1ppm at 20% strain at 40°C for 100 hours

No cracking visible

by eye

Seawater Resistance

DIN 86076, Section 7.7

28 days in artificial

seawater at 95°C ±2°C

Hardness ±10° (Max)

Shore A

Volume +10/-5% (Max)

Abrasion Resistance

BS 903.A9

Method B, 1000

revolutions

0.5cc (Max)

DIN 53516

100mm3 (Max)

Bond Strength

Steel to Rubber

BS 903.A21

Method B

7N/mm (Min)